Vinyl monomers bearing sulfonyl(trifluoromethane sulfonyl) imide group: synthesis and polymerization using nitroxide-mediated polymerization - Aix-Marseille Université Access content directly
Journal Articles Polymer Chemistry Year : 2016

Vinyl monomers bearing sulfonyl(trifluoromethane sulfonyl) imide group: synthesis and polymerization using nitroxide-mediated polymerization

Abstract

A series of water-soluble styrene and propyl (meth)acrylate based monomers bearing a sulfonyl(trifluoromethane sulfonyl) imide (STFSI) group was prepared. These monomers were synthesized in good yield from the corresponding chloride sulfonyl monomer and trifluoromethanesulfonamide. Their chemical structures were further confirmed by HR-MS and NMR spectroscopy. Nitroxide-mediated polymerization of the prepared monomers was then performed in aqueous solution at 100 °C, 90 °C and 75 °C for acrylate, styrene and methacrylate derivatives, respectively. Controlled polymerization was successfully achieved as illustrated by the linearity of ln([M]0/[M]) vs. t2/3, the molar mass increase with conversion and the relatively low dispersity values for the resulting homopolymers. Compared to their neutral analogous polymers, the prepared anionic homopolymers exhibited a higher glass-transition temperature. This phenomenon was attributed to the electrostatic interactions between STFSI side groups along the polymer backbone.

Domains

Polymers
Fichier principal
Vignette du fichier
c6py01004k.pdf (2.38 Mo) Télécharger le fichier
Origin : Publication funded by an institution
Loading...

Dates and versions

hal-01497309 , version 1 (28-03-2017)

Licence

Attribution - NonCommercial

Identifiers

Cite

Trang N. T. Phan, Adèle Ferrand, Hien The Ho, Livie Liénafa, Marion Rollet, et al.. Vinyl monomers bearing sulfonyl(trifluoromethane sulfonyl) imide group: synthesis and polymerization using nitroxide-mediated polymerization. Polymer Chemistry, 2016, 7 (45), pp.6901-6910. ⟨10.1039/c6py01004k⟩. ⟨hal-01497309⟩
318 View
573 Download

Altmetric

Share

Gmail Facebook X LinkedIn More